Abstract
Microstructured molds are essential for fabricating various components ranging from precision optics and microstructured surfaces to microfluidics. However, conventional fabrication technology such as photolithography requires expensive equipment and a large number of processing steps. Here, we report a facile method to fabricate micromolds based on a reusable photoresponsive hydrogel: Uniform micropatterns are engraved into the hydrogel surface using photo masks under UV irradiation within a few minutes. Patterns are replicated using polydimethylsiloxane with minimum feature size of 40 μm and smoothness of Rq ~ 3.4 nm. After replication, the patterns can be fully erased by light thus allowing for reuse as a new mold without notable loss in performance. Utilizing greyscale lithography, patterns with different height levels can be produced within the same exposure step. We demonstrate the versatility of this method by fabricating diffractive optical elements devices and a microlens array and microfluidic device with 100 µm wide channels.
Similar content being viewed by others
Introduction
Micromolds play an important role in polymer replication to, e.g., fabricate surfaces with special wetting properties1,2,3, microfluidic devices4,5,6,7, high-sensitivity sensors8,9, or mirooptics10,11,12. However, photolithography, which is the most widely used method to generate micromolds, suffers from several disadvantages, most prominently the multiple-step nature of the process, the requirement for sophisticated devices and the fact that larger amounts of toxic waste is produced during processing13. Therefore, versatile methods for the creation of inexpensive molds are highly sought-after. Hydrogels, owing to their easily tailorable physical and chemical properties, exhibit promising application potentials in various engineering fields, and have been used as molds for polymer replication. For example, Hirama et al.14,15 and Sugiura et al.16 manually arranged hydrogel molds and covered them using polydimethylsiloxane (PDMS). After curing PDMS, the hydrogel molds were washed out using hot water to fabricate microchannels. Similarly, by embedding flexible gel wires with high mechanical strength in PDMS solution and consecutively pulling out the gel templates from the cured PDMS matrix, three-dimensional (3D) microchannels with different cross sections were fabricated. However, in these methods, the gel templates need to be manually arranged, which is inconvenient and suffers from low precision. Using pre-gel solution as the photoresist, Dang et al.17 prepared hydrogel molds for polymer replication via mask-assisted photopolymerization, which are suitable for large area fabrication, but the over-exposure between adjacent structures resulted in limited resolution. Overall, owing to its flexibility which enables easy demolding and smooth surface, exploring better ways to utilize hydrogel as micromolds for polymer replication is a very promising approach.
Responsive hydrogels can be controlled by external stimulus and can exhibit biomimetic behaviors which has gained significant attention from the scientific community, e.g., for the creation of soft robots18,19,20,21, wearable electronics22,23, and medical devices24,25. Particularly, the use of soft materials like hydrogels, swollen polymer networks for generation of microstructures leads to Gaussian feature26,27. Such profiles are useful for generating smooth gradients, e.g. optical elements28,29 as well as biomimetic structures for cells30, which often require curved surfaces. Among them, photoresponsive hydrogels are particularly attractive because light as the stimulus exhibits many advantages. Light patterns can be generated at high resolutions and in very controllable fashion, are non-invasive, and offer the possibility for fast stimulus switches (on/off) with virtually no delay31,32,33. Volume change is a common responsive behavior of photoresponsive hydrogel under visible (VIS) or ultraviolet (UV) light. Overall, there are two pathways for preparing and utilizing photoresponsive hydrogels. Firstly, the macroscopic shape change of the hydrogel upon exposure can be used to generate actuated components for soft robotics34,35,36, reversible microfluidic valves37,38, and controllable drug delivery system39. Secondly, mask-assisted selective irradiation can be used to generate hydrogels with switchable surface topographies. As an example, Kuenstler et al.40 fabricated a photoresponsive hydrogel based on the host-guest complex between cyclodextrins and azobenzene groups which shows reversible wetting property changes owing to isomerization41,42,43. Via photo-induced localized swelling/deswelling of the network, the hydrogel sheet changed its topography reversibly. Stumpel et al.44 firstly prepared a hydrogel containing spiropyran with varying crosslinking density. After swelling, a patterned hydrogel surface was obtained due to the different crosslinking-density-dependent swelling abilities. Under visible light exposure, the topography of the surface changed as a result of photoinduced deswelling of the hydrogel network. In addition, Han et al. recently demonstrated that laser projection via a digital micromirror device (DMD) can directly change the network structure of polyacrylate-based hydrogels, which is subsequently utilized to guide the assemble of nanoparticles to form designed 2D or 3D structures showing promising application as optical microdevices, like diffractive optical elements (DOE)45. We reasoned that similar approaches should be applicable for generating micromolds similar to the conventional processing pipeline using photolithography. In photolithography, a photosensitive polymer (i.e., a photoresist) is structured using selective irradiation, mostly using photomasks. Depending on the nature of the photoresist (positive- or negative-type), the irradiated areas (in positive-type photoresists) or the non-exposed areas (in negative-type photoresists) can be removed in a subsequent development step. The obtained physical structure is then used as a micromold for the generation of, e.g., microoptical components such as lenses or lens arrays. The disadvantage of this workflow is that the structure, once defined, cannot be changed and a different micromold must be generated for every design. In contrast to this, we reasoned that a photoswitchable hydrogel surface, where a surface topography could be generated by photo-induced localized swelling/deswelling as a consequence of light exposure should allow the generation of a reconfigurable micromold, i.e., a mold which can be set and reset multiple times (Fig. 1a). We refer to these reusable and reconfigurable micromolds as micromold displays reflecting their ability to be dynamically set and reset.
In this work, we present a facile method to generate micromold displays based on the photoresponsive acrylamide/azobenzene-cyclodextrin (AM/AZO-CD) hydrogel prepared via thermal radical polymerization and their usage in polymer replication. Micromolds with different profiles and sizes can be formed easily and quickly on the hydrogel surface and replicated with high fidelity onto PDMS components. In contrast to classical photolithography, this process requires no development step, drying or subsequent etching processes or substances such as potassium hydroxide or hydrofluoric acid which are standard in classical micromold generation. Owing to the reversibility of azobenzene-cyclodextrin (AZO-CD) host-guest interaction36,40, the patterned hydrogel can be reused at least four times by erasing the original structure using visible light. Utilizing a custom-made lithography system based on a DMD, patterns with a wide variety of feature sizes and geometries can be realized directly on the hydrogel surface at low cost and within a few minutes. Using a grayscale digital light processing (DLP), grayscale lithography can be conveniently carried out to prepare micropatterns with different heights in one step. Furthermore, we demonstrate the applicability of the method by fabrication of a microfluidic device and a microlens array and high-performance diffractive optical elements (DOE) using the micromold display
Results
Micromold display fabrication
The photoresponsive AM/AZO-CD hydrogel is fabricated via thermal radical polymerization. Firstly, the organic gel is synthesized via co-polymerization of acrylamide (AM) and 4-methacryloyloxyazobenzene (AZO). 2,2’-azobis(2-methylpropionitrile) (AIBN) and N,N’-methylenebisacrylamide (MBA) are chosen as the thermal initiator and crosslinker, respectively. The obtained gel (Supplementary Fig. 2a) is then immersed in α-cyclodextrin (α-CD) solution for solvent exchange. During this process, trans-azobenzene forms a complex with α-CD because of host-guest interaction40,46. Due to the hydrophilic outer surface of the α-CD unit, the network becomes more hydrophilic once the α-CD units cover the hydrophobic azobenzene units. In this state, the gel absorbs more water and reaches a fully-swollen state (Fig. 1b) with a swelling ratio of about 55 wt% (Supplementary Fig. 2b). Tran-cis isomerization of azobenzene happens upon illumination with UV light. Because of its different spatial structure, cis-azobenzene groups slip out from α-CD cavity, leaving more hydrophobic constituents exposed to the surrounding water environment. As a result, water is partially repelled from the network resulting in a shrunken hydrogel (Fig. 1b). A free thin hydrogel film shrinks by 16.9 ± 0.6 vol% in-plane (X/Y) and 16.3 ± 0.7 vol% out-of-plane (Z-direction, see Supplementary Fig. 3a & b). The trans-cis isomerization was confirmed via ultraviolet-visible (UV-VIS) absorption spectroscopy of the AM/AZO-CD hydrogel (Supplementary Fig. 4a & b). The intensity of the characteristic absorption peak of trans-azobenzene groups at 323 nm decreases gradually when illuminating the hydrogel with UV light (320–400 nm, 4.6 mW cm−2) and recovers to original intensity under VIS light illumination (400-700 nm, 4.9 mW cm−2). After five cycles, the absorption peak at 323 nm shows little change (below 6%) exhibiting good reversibility and stability (Supplementary Fig. 4c).
To enable high-resolution micromold displays, the gel is prepared as a uniform, smooth film of 1 mm thickness on a glass slide. For doing so, two glass slides are spaced with an adjustable spacer (made from silicone rubber) and the AM/AZO-CD hydrogel is prepared in between them (Supplementary Fig. 5). The bottom glass slide is functionalized with 3-methacryloxypropyl dimethylchlorosilane (MACS) to covalently attach the polymerized gel onto the glass substrate. The polymerized gel is stored in α-CD solution for 24 h to reach swelling balance. Subsequently, the gel is exposed to UV light (320–400 nm or 300–400 nm, Fig. 1a), structured either by a physical mask or by an in-house developed maskless projection lithography system based on a DMD device47. The illuminated areas of the hydrogel become more hydrophobic, which causes local shrinkage in the hydrogel (Fig. 1a, b) and results in a microstructured gel surface and thus a micromold. The microstructure on the gel was analyzed by white light interferometry (WLI). After 1 min mask-assisted UV irradiation, a uniform microstructure is generated on the hydrogel surface (Fig. 1c). To emphasize the stability of the engraved structure on the gel, it was left in α-CD solution without extra protection to prevent ambient light and analyzed again 1 h after UV illumination. No detectable changes were observed in the gel structure (Supplementary Fig. 6). In order to demonstrate the ability of this structure to function as a micromold, PDMS replication was carried out. For this, water on the hydrogel surface is gently removed using a nitrogen gun. The PDMS precursor is then poured onto the microstructured hydrogel surface. After curing, the microstructured PDMS can be easily peeled off from the hydrogel micromold. The replicated PDMS structure was also analyzed by WLI (Fig. 1d). Cross-sectional profiles of the hydrogel micromold and the replicated PDMS were compared (Supplementary Fig. 7), and the data shows that the microstructure on the hydrogel surface is replicated with high fidelity with features as fine as 40 µm. The surface generated shows low surface roughness with a Ra of 2.68 nm and Rq of 3.4 nm (Fig. 1e) as determined by atomic force microscopy (AFM). In addition, the prepared hydrogel can be stored for long time in the glass cell (at least 5 months) without noticeable loss the performance, which is desirable in practical applications. To verify this, a micro-square array was structured onto the freshly prepared hydrogel and the hydrogel stored for 5 months using a physical mask (illumination time 10 s), the obtained structures show no difference (Supporting information Fig. 8).
Repeated setting and resetting of the micromold display
As stated, the reversible nature of the gels allows micromold displays to be structured, reset and structured using different patterns. In order to allow multiple setting/resetting cycles, the chemical composition of the gels was investigated and adjusted. A balance between gel stiffness for easy handling and gel softness for increased depth of the generated microstructures, as well as illumination time for fast processing, was sought. By adjusting the crosslinker (MBA) molar ratio between 1.2 mol%, 1.6 mol%, and 2 mol% in the gel, the elastic modulus of the hydrogel was modulated from 18 kPa to 27 kPa, as determined by AFM (Fig. 2a). A low modulus as in a soft gel of 1.2 mol% crosslinker enables the formation of deeper microstructures, with a depth of 10 µm formed within 5 min of illumination for a square array pattern (width 100 μm, gap 100 μm) (Fig. 2b). However, higher softness causes the hydrogel vulnerable to adhesion force between the hydrogel and the cover slide when opening the glass cell (Supplementary Fig. 5) in which the gel was polymerized, which relatively makes it more difficult to obtain hydrogel with high surface quality. In contrast, higher crosslinking density (up to 2 mol% of crosslinker ratio) allows gels with higher elastic modulus and improved mechanical resilience, but reduced engraving speed (Fig. 2b). As a compromise, a gel with 1.6 mol% crosslinker ratio was chosen. For this variant, an engraving depth of 10.3 μm after 15 min exposure could be achieved (Fig. 2c) while providing excellent mechanical resilience during manufacturing and better handling of the micromold displays.
The reversibility of the micromold display was demonstrated by consecutive PDMS replications (Fig. 2d). A first pattern was engraved on the micromold display and consecutively used for PDMS replication. The display was then immersed into α-CD solution and illuminated for 1 h under VIS light (400–700 nm). After 48 h of storing in the dark, the generated pattern was completely erased and the display was thus reset. Subsequently, a second pattern was generated, replicated and erased in the same manner. The process was performed for 4 times, and pictures of consecutively replicated PDMS pattern and profiles based on WLI characterization of each replicated structures are shown in Fig. 2e, demonstrating the full reversibility of the setting as well as the reproducibility across several set/reset cycles.
In addition, the versatility of the hydrogel micro-molds was also demonstrated by engraving a butterfly structure on the curved cylindrical hydrogel surface, then, the engraved structure was successfully replicated using PDMS (Supplementary Fig. 9a, b), which is desirable in many engineering fields, like optical device fabrication48.
Micromold display via grayscale projection lithography
Maskless projection lithography enables high-resolution illumination without generation of a greyscale physical mask. Using a DMD, greyscale lithography is implemented using pulse-width modulation of the mirrors. Figure 3a illustrates the principle of using maskless projection lithography for the structuring of the micromold display using a custom-made DMD47. A triangle array pattern was created on the micromold displays, and replicated into a PDMS film (Fig. 3b). Benchmarking the lateral resolution on the DMD setup, we found that square arrays with a width and gap of 40 μm can be replicated with good fidelity. Smaller sizes caused structures to blend together and become indistinguishable (Supplementary Fig. 10). A square array pattern (width 100 μm, gap 100 μm) was used to test the engraving speed on the micromold display based on the DMD setup, the engraving depth of the gel quickly and linearly increased to 8 μm within roughly 90 s before slowly reaching to 11 μm after 10 min illumination (Fig. 3c). This phenomenon is, on the one hand, owing to the limited UV penetration ability, the very top hydrogel surface receives the highest exposure energy to induce the isomerization of azobenzene groups and results in rapid growth speed of the engraved structure. With increasing depth into the hydrogel, the received exposure energy reduced reduces gradually, and the growth speed decreased correspondingly. On the other hand, the contraction of the exposed area is constrained by the ambient polymer network, the constrain force increases with larger contraction, which also contribute the slower growing speed with increasing exposure time. Similar phenomenon has been reported when fabricating microstructures on a soft photo responsive substrate26,27. In addition to uniform structure arrays, digital masks with arbitrary structures, a tree for example, can be easily designed and used to engrave patterns on the micromold display, and then be replicated using PDMS (illumination time: 120 s, Fig. 3d). As demonstrated with the physical mask-based setup, the micromold displays could be repeatedly set and reset using the DMD setup as well (illumination time: 120 s, Fig. 3e, f). In addition, as shown in supplementary Fig. 11, the hydrogel shows no significant fatigue after 6 times structuring-erasing cycles, which shows its stable ability to be restructured as micromolds. The maskless DMD setup was further used for grayscale lithography which gives the ability to modulate the projected light intensity in spatially controlled fashion. This allows varying the local volumetric change on the micromold display as a function of the set grayscale value during the UV exposure. As an example, a square array was projected with different greyscale values (Supplementary Fig. 12) for the squares (Fig. 3g), resulting in patterns with different height for every single square (illumination time: 120 s). The SEM images of obtained microstructures show decent surface quality (Supplementary Fig. 13). Utilizing an annular grayscale digital mask, a staircase structure of 6.7 µm with three height levels was fabricated within 20 s (Supplementary Fig. 14). Besides grayscale masks with uniform shapes and simple grayscale gradient, a multiple grayscale flower image (Fig. 3h) was used to generate a micromold with complex structure (illumination time: 30 s). The PDMS structure replicated from the micromold display shows the analogous flower structure with different heights following the grayscale image.
Optical and microfluidic devices fabrication
Without requiring any sophisticated devices or hazardous chemicals, the developed micromold displays represent an easily accessible method for microstructuring and soft lithography, affording structuring such as, e.g., microoptical or microfluidic devices. As an example, a microlens array was generated by illuminating the micromold display via a circle array physical mask. The replicated PDMS microlens array shows uniform structures (Fig. 4a, b) and the intended clear diffraction pattern (laser source: 532 nm) (Fig. 4c). To further highlight the versatile application of the micromold display in optical engineering field, DOE devices with complex microstructured surface were fabricated to reconstruct arbitrary user-defined patterns. Firstly, a binary hologram (Fig. 4d) was generated using Gerchberg-Saxton (GS) algorithm45,49,50 by inputting the designed image like a dolphin (inset of Fig. 4d) as the source file. The generated hologram was then used as the digital mask and input into the homemade projection lithography system for engraving structures onto the hydrogel surface for PDMS replication. Figure 4e shows the 3D profile of the replicated PDMS structure with feature resolutions of about 30 μm and the corresponding diffraction pattern (Fig. 4f, laser source: 650 nm). Holograms of various patterns such as a butterfly image and the IMTEK logo could be generated for engraving structures onto the hydrogel surface, and the replicated PMDS DOE devices showed high performance to display the designed patterns vividly (Supplementary Fig. 15).
In addition to the optical devices, we fabricated a digital mask for a microfluidic diffusive mixer structure for usage of the micromold display. The illuminated micromold display was then used as the master for PDMS replication. As shown in Fig. 4g and Fig. 4h, the obtained serpentine microchannel in the replicated PDMS exhibited uniform width (100 μm) and depth (20 μm) at different areas throughout the pattern. To test the performance of the channel, the PDMS replica was bonded onto a glass slide and dyed water with different colors was injected into the two mixer inlets. The diffusive mixing could be clearly observed throughout the meander channel structure (Fig. 4i). As an alternative, a microfluidic chip can be generated only requiring a single replication step which shows same performance although with lower depth (Supplementary Fig. 16).
Discussion
In this paper, we developed a micromold display based on AM/AZO-CD photoresponsive hydrogels which allow the generation of masters, e.g., for polymer replication circumventing the laborious, cost- and waste-intensive workflows commonly associated with photolithography. The micromold display makes use of the localized contraction induced by spatially controlled UV illumination of the gel, which engraves microstructures into the hydrogel within a few minutes, thus significantly simplifying classic replication process workflows. Besides the generation of binary (single-height) microstructures with tens of micron resolution, the developed micromold display also allows for greyscale patterning, creating different height levels in one illumination step, which allows the generation of replication master structures with different height levels as required, e.g., for the fabrication of microlens arrays. We demonstrated the ability to design microlens arrays using grayscale lithography to generate gradient patterns in the micromold displays; and high-performance DOE devices with complex microstructure are fabricated to display arbitrary user-designed patterns under coherent laser source. Furthermore, for demonstrating the capabilities of the micromold displays or the generation of high-resolution structures, a microfluidic device was fabricated with uniform width and depth throughout the whole channel. Usage of the micromold displays alleviates the necessity for expensive cleanroom-based photolithography, toxic solutions and cost-intensive photoresins. We believe that this platform can become a valuable tool for microengineering, biotechnology, clinical analytics and miniaturization, effectively providing access to a simple, reusable device for the generation of replication masters in polymer molding, soft lithography, UV casting and similar processes.
Methods
Materials
Acrylamide (AM, 99%), α-cyclodextrin (α-CD, 99%), 4-phenylazopheonl (98%), methacrylic anhydride (94%), 2,2′-azobis(2-methylpropionitrile) (AIBN, 98%), N,N’-methylenebisacrylamide (MBA, 99%), 4-dimethylaminopyridine (DMAP, 98%), sodium chloride (NaCl, 99%), magnesium sulfate (MgSO4, 98%) were purchased from Sigma-Aldrich, Germany. Methanol (99.9%), dimethyl sulfoxide (DMSO, 99.5%), tetrahydrofuran (THF, 99.5%) were purchased from Carl Roth, Germany; 3-methacryloxypropyl dimethylchlorosilane (MACS, 92%) and 1H,1H,2H,2H-perfluoroctyldimethylchlorosilane (97%) were purchased from Abcr GmbH, Germany. Polydimethylsiloxane (PDMS, 601 A and 601B) was purchased from Wacker, Germany. Transparent silicon rubber sheet was purchased from Technikplaza, Germany.
Synthesis of 4-methacryloyloxy azobenzene monomer
4-methacryloyloxy azobenzene (AZO) monomer is synthesized according to a modified method as reported in literature2. 4-phenylazopheonl (7.92 g, 0.04 mol, 1 eq.), methacrylic anhydride (7.392 g, 0.048 mol, 1.2 eq.), DMAP (100 mg) were dissolved in 50 mL dried THF in a round-bottom flask. The mixture was stirred at 50 °C for 20 h and then cooled to room temperature. After being washed with saturated NaCl solution for three times, the oil phase was dried using MgSO4 and evaporated to obtained the crude product. The crude product was recrystallized in methanol twice to obtained the pure AZO monomer (yield: 83%), and NMR result (250 MHz, Bruker, USA) shows no impurity (Supplementary Fig. 1).
Preparation of AM/AZO-CD hydrogel
AM/AZO-CD hydrogels with different crosslinker content were prepared. As an example, AM/AZO-CD hydrogel with 1.6 mol% crosslinker was prepared dissolving 2130 mg AM, 240 mg AZO monomer, 73.92 mg MBA and 39.36 mg AIBN in DMSO to obtain a clear pre-gel solution. The solution was injected into a sandwich glass cell composed of a common glass slide, a MACS modified glass slide prepared based on a reported method51 and a PDMS spacer (Supplementary Fig. 5). The polymerization was carried out in an oven (47° C) for 72 h. After removing the glass slide, the gel was immersed into α-CD/H2O solution (25 mg mL−1) for 24 h to reach the fully-swollen state.
For 3D lithography on curved hydrogel surface, the pre-gel solution prepared above was injected into a glass tube (inner diameter: 15 mm). The glass tube was sealed and put into the oven (47 °C) for 72 h for polymerization. A cylindrical hydrogel was obtained by breaking the glass tube after polymerization, and was immersed into α-CD/H2O solution (25 mg mL−1) for 24 h to reach the fully-swollen state.
The swelling ratio of the AM/AZO-CD gel was calculated according to the function: SR = (Wt-Wo)/Wo X 100%. Where, SR is the swelling ratio, Wo is the original weight of the gel and Wt is the real-time weight measured after immersing the gel into α-CD for different times.
Lithography of the micromold display, structure replication, and erasing of the displayed structure
For mask-based lithography, the hydrogel was immersed in α-CD/H2O solution and covered with the physical mask with a light intensity of 4.6 mW cm−2 (wavelength: 320-400 nm). For maskless projection lithography, the digital pattern was projected onto the hydrogel via a custom-made maskless lithography system based on a DMD47 using a light intensity of 3.2 mW cm−2 at 300–400 nm. After exposure, remaining water on the AM/AZO-CD hydrogel surface was gently removed using a nitrogen gun. PDMS was mixed and degassed according the manufacturer and poured onto the micromold display surface and left to cure for 6 h at room temperature. Subsequently, the cured PDMS was peeled off from the hydrogel surface to obtain the replicated structure. After replication, the hydrogel was immersed in α-CD/H2O solution and illuminated with VIS light (400–700 nm, 4.9 mW cm−2) for 1 h, and then stored in a dark environment for 48 h to recover its original state.
Microfluidic device and microlens array fabrication
A microchannel pattern was first created on the micromold display using a physical mask under UV light (time: 5 min, 320–400 nm, 4.6 mW cm−2) before replicating the displayed structure into PDMS to obtain the positive mold. The positive structured PDMS template was then treated using a handheld corona discharge (BD-20V, 230 V, 50/60 Hz, Electro-Technic Products Inc., USA)52 for 30 s and immersed into the 1H,1H,2H,2H-perfluoroctyldimethylchlorosilane solution (3 v/v% in toluene) for 10 min. After being washed with isopropanol and completely dried in an oven at 100 °C for 30 min, another layer of PDMS resin was poured on the obtained positive PDMS model and peeled off after being cured. The obtained PDMS microchannel was washed with isopropanol and processed using corona discharge (30 s). It was then placed on a clean glass slide freshly treated using corona discharge (30 s) and cured under a pressure in an oven (100 °C) for 1 h.
The microlens structure was firstly engraved on the micromold display using a physical circle array mask (diameter/gap: 50/100 μm) under UV light (320-400 nm, 4.6 mW cm−2) for 15 min. The structure was then replicated into PDMS using the described procedure.
Characterization
UV-VIS absorption of AM/AZO-CD hydrogel was carried out using a UV-VIS spectrophotometer (Evolution 201, Thermofisher, Germany). The surface structure of the micromold display and the replicated PDMS was characterized using a white light interferometry (WLI, Newview 9000, Zygo, Germany) and scanning electron microscope (SEM, Tescan Amber X, Czech Republic). Youngs modulus of hydrogels was characterized using atomic force microscopy (AFM) (JPK Nanowizard 4, Bruker, Germany), and roughness of the replicated PDMS structures was characterized using AFM (Multimode 8, Bruker, Germany).
Data availability
Source Data file has been deposited in Figshare under accession code DOI link: https://doi.org/10.6084/m9.figshare.25726524.
References
Wang, Y. Z. et al. Smart superhydrophobic shape memory adhesive surface toward selective capture/release of microdroplets. ACS Appl. Mater. Interfaces 11, 10988–10997 (2019).
Cheng, Z. J. et al. Superhydrophobic shape memory polymer arrays with switchable isotropic/anisotropic wetting. Adv. Funct. Mater. 28, 11 (2018).
Pirani, F., Angelini, A., Ricciardi, S., Frascella, F. & Descrovi, E. Laser-induced anisotropic wettability on azopolymeric micro-structures. Appl. Phys. Lett. https://doi.org/10.1063/1.4978260 (2017).
Ma, Y., Thiele, J., Abdelmohsen, L., Xu, J. & Huck, W. T. Biocompatible macro-initiators controlling radical retention in microfluidic on-chip photo-polymerization of water-in-oil emulsions. Chem. Commun. 50, 112–114 (2014).
Yuk, H., Zhang, T., Parada, G. A., Liu, X. & Zhao, X. Skin-inspired hydrogel–elastomer hybrids with robust interfaces and functional microstructures. Nat. Commun. 7, 12028 (2016).
Li, Y., Motschman, J. D., Kelly, S. T. & Yellen, B. B. Injection molded microfluidics for establishing high-density single cell arrays in an open hydrogel format. Anal. Chem. 92, 2794–2801 (2020).
Lin, P. H. & Li, B. R. Passively driven microfluidic device with simple operation in the development of nanolitre droplet assay in nucleic acid detection. Sci. Rep. 11, 21019 (2021).
Pang, C. et al. Highly skin-conformal microhairy sensor for pulse signal amplification. Adv. Mater. 27, 634–640 (2015).
Mannsfeld, S. C. et al. Highly sensitive flexible pressure sensors with microstructured rubber dielectric layers. Nat. Mater. 9, 859–864 (2010).
Mader, M. et al. High-throughput injection molding of transparent fused silica glass. Science 372, 182–186 (2021).
Albero, J. et al. Fabrication of spherical microlenses by a combination of isotropic wet etching of silicon and molding techniques. Opt. Express 17, 6283–6292, (2009).
Bitterli, R. et al. Fabrication and characterization of linear diffusers based on concave micro lens arrays. Opt. Express 18, 14251–14261, (2010).
Qin, D., Xia, Y. & Whitesides, G. M. Soft lithography for micro- and nanoscale patterning. Nat. Protoc. 5, 491–502 (2010).
Hirama, H., Odera, T., Torii, T. & Moriguchi, H. A lithography-free procedure for fabricating three-dimensional microchannels using hydrogel molds. Biomed. Microdevices 14, 689–697 (2012).
Hirama, H. et al. Rapid prototyping of a nanoparticle concentrator using a hydrogel molding method. Polymers. https://doi.org/10.3390/polym13071069 (2021).
Sugiura, Y., Hirama, H. & Torii, T. Fabrication of microfluidic valves using a hydrogel molding method. Sci. Rep. 5, 13375 (2015).
Dang, T.-D., Kim, Y. H., Choi, J. H. & Kim, G.-M. A novel simple preparation method of a hydrogel mold for PDMS micro-fluidic device fabrication. J. Micromechanics and Microeng. https://doi.org/10.1088/0960-1317/22/1/015017 (2012).
Huang, J. et al. Electrically programmable adhesive hydrogels for climbing robots. Sci. Robot. 6, eabe1858 (2021).
Zhu, C. N. et al. Reconstructable gradient structures and reprogrammable 3D deformations of hydrogels with coumarin units as the photolabile crosslinks. Adv. Mater. 33, e2008057 (2021).
Na, H. et al. Hydrogel-based strong and fast actuators by electroosmotic turgor pressure. Science 376, 301–307 (2022).
Ni, C., Chen, D., Zhang, Y., Xie, T. & Zhao, Q. Autonomous shapeshifting hydrogels via temporal programming of photoswitchable dynamic network. Chem. Mater. 33, 2046–2053 (2021).
Dobashi, Y. et al. Piezoionic mechanoreceptors: force-induced current generation in hydrogels. Science 376, 502–507 (2022).
Xia, S., Song, S., Jia, F. & Gao, G. A flexible, adhesive and self-healable hydrogel-based wearable strain sensor for human motion and physiological signal monitoring. J. Mater. Chem. B 7, 4638–4648 (2019).
Shi, S. et al. An innovative solvent-responsive coiling–expanding stent. Adv. Mater. https://doi.org/10.1002/adma.202101005 (2021).
Kim, S.-K. et al. Bimetallic nanocatalysts immobilized in nanoporous hydrogels for long-term robust continuous glucose monitoring of smart contact lens. Adv. Mater. 34, 2110536 (2022).
Chen, D. et al. Homeostatic growth of dynamic covalent polymer network toward ultrafast direct soft lithography. Sci. Adv. https://doi.org/10.1126/sciadv.abi7360 (2021).
Li, T. et al. Hierarchical 3D patterns with dynamic wrinkles produced by a photocontrolled diels–alder reaction on the surface. Adv. Mater. https://doi.org/10.1002/adma.201906712 (2020).
Aldalali, B., Kanhere, A., Fernandes, J., Huang, C.-C. & Jiang, H. Fabrication of polydimethylsiloxane microlenses utilizing hydrogel shrinkage and a single molding step. Micromachines 5, 275–288 (2014).
Dong, L., Agarwal, A. K., Beebe, D. J. & Jiang, H. Adaptive liquid microlenses activated by stimuli-responsive hydrogels. Nature 442, 551–554 (2006).
Esch, M. B., Post, D. J., Shuler, M. L. & Stokol, T. Characterization of in vitro endothelial linings grown within microfluidic channels. Tissue Eng. Part A 17, 2965–2971 (2011).
Jiang, Z. et al. Strong, self-healable, and recyclable visible-light-responsive hydrogel actuators. Angew. Chem. -Int. Ed. 59, 7049–7056 (2020).
Stumpel, J. E., Liu, D. Q., Broer, D. J. & Schenning, A. Photoswitchable hydrogel surface topographies by polymerisation-induced diffusion. Chem. -Eur. J. 19, 10922–10927 (2013).
Dong, Y. Q. et al. Engineering the cell microenvironment using novel photoresponsive hydrogels. ACS Appl. Mater. Interfaces 10, 12374–12389 (2018).
Li, C. et al. Supramolecular-covalent hybrid polymers for light-activated mechanical actuation. Nat. Mater. 19, 900 (2020).
Li, C., Iscen, A., Palmer, L. C., Schatz, G. C. & Stupp, S. I. Light-driven expansion of spiropyran hydrogels. J. Am. Chem. Soc. 142, 8447–8453 (2020).
Iwaso, K., Takashima, Y. & Harada, A. Fast response dry-type artificial molecular muscles with [c2]daisy chains. Nat. Chem. 8, 625–632 (2016).
ter Schiphorst, J. et al. Photoresponsive passive micromixers based on spiropyran size-tunable hydrogels. Macromol. Rapid Commun. 39, 6 (2018).
ter Schiphorst, J. et al. Molecular design of light-responsive hydrogels, for in situ generation of fast and reversible valves for microfluidic applications. Chem. Mater. 27, 5925–5931 (2015).
Kim, H. et al. Visible light-triggered on-demand drug release from hybrid hydrogels and its application in transdermal patches. Adv. Health. Mater. 4, 2071–2077 (2015).
Kuenstler, A. S. et al. Reconfiguring gaussian curvature of hydrogel sheets with photoswitchable host-guest interactions. ACS Macro Lett. 9, 1172–1177 (2020).
Sarkar, N., Bhattacharjee, S. & Sivaram, S. Surface functionalization of poly(ethylene) with succinic anhydride: preparation, modification, and characterization. Langmuir 13, 4142–4149 (1997).
Raduge, C., Papastavrou, G., Kurth, D. G. & Motschmann, H. Controlling wettability by light: illuminating the molecular mechanism. Eur. Phys. J. E Soft Matter 10, 103–114 (2003).
Delorme, N., Bardeau, J. F., Bulou, A. & Poncin-Epaillard, F. Azobenzene-containing monolayer with photoswitchable wettability. Langmuir 21, 12278–12282 (2005).
Stumpel, J. E. et al. Photoswitchable ratchet surface topographies based on self-protonating spiropyran-NIPAAM hydrogels. ACS Appl. Mater. Interfaces 6, 7268–7274 (2014).
Han, F. et al. Three-dimensional nanofabrication via ultrafast laser patterning and kinetically regulated material assembly. Science 378, 1325–1331 (2022).
Yamaguchi, H. et al. Photoswitchable gel assembly based on molecular recognition. Nat. Commun. https://doi.org/10.1038/ncomms1617 (2012).
Waldbaur, A., Waterkotte, B., Schmitz, K. & Rapp, B. E. Maskless projection lithography for the fast and flexible generation of grayscale protein patterns. Small 8, 1570–1578 (2012).
Zhang, D., Yu, W., Wang, T., Lu, Z. & Sun, Q. Fabrication of diffractive optical elements on 3-D curved surfaces by capillary force lithography. Opt. Express 18, 15009–15016, (2010).
Sandford O’Neill, J. et al. 3D Switchable diffractive optical elements fabricated with two‐photon polymerization. Adv. Opt. Mater. https://doi.org/10.1002/adom.202102446 (2022).
Xiong, Z., Kunwar, P. & Soman, P. Hydrogel-based diffractive optical elements (hDOEs) using rapid digital photopatterning. Adv. Opt. Mater. https://doi.org/10.1002/adom.202001217 (2021).
Kotz, F. et al. Three-dimensional printing of transparent fused silica glass. Nature 544, 337–339 (2017).
Haubert, K., Drier, T. & Beebe, D. PDMS bonding by means of a portable, low-cost corona system. Lab Chip 6, 1548–1549, (2006).
Acknowledgements
This work is supported by the Deutsche Forschungsgemeinschaft (DFG, German Research Foundation) under Germany’s Excellence Strategy – EXC−2193/1 – 390951807, the European Research Council (ERC) under the European Union’s Horizon 2020 research and innovation program (grant agreement no. 816006), and the Research Cluster “Interactive and Programmable Materials (IPROM)” funded by the Carl Zeiss Foundation.
Funding
Open Access funding enabled and organized by Projekt DEAL.
Author information
Authors and Affiliations
Contributions
B.E.R. and D.H. conceived the idea. P.Z. designed the experiments. P.Z., Q.S., S.B., F.M., A.G., N.N., M.S., P.H., and S.T. performed the experiments. P.Z. analyzed the results. P.Z., D.H., F.K., and B.E.R. drafted the manuscript, and all authors contributed to writing the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Peer review
Peer review information
Nature Communications thanks Arnaud Bertsch, Caterina Credi and the other, anonymous, reviewer(s) for their contribution to the peer review of this work. A peer review file is available.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Zhu, P., Song, Q., Bhagwat, S. et al. Generation of precision microstructures based on reconfigurable photoresponsive hydrogels for high-resolution polymer replication and microoptics. Nat Commun 15, 5673 (2024). https://doi.org/10.1038/s41467-024-50008-6
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-024-50008-6
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.